Ultra-clear glass
Common float glass looks green to certain degree. Especially when the glass is thickened or piled together, such phenomenon is more obvious. At present, the architectural designers have required higher optical requirements for the permeability of glass, thus the low-iron glasses occurred. Ultra-clear glass has very strong light transmittance. Its perfect transparency assures you to be able to obtain more perfect visual effect of natural color.
Visual comparison of low-iron glass and common glass
Dimensions of ultra-clear glass:
Max. Size: 2440 MM X 3660 MM
Min. Size: 300 MM X 300 MM
The Range of Thickness:Toughened glass 4 MM ~ 19 MM
Application Range of ultra-clear glass:
Show case of museum, large theatre, counter of gold shop, hall of hotel, partition of ball, point-supporting curtain wall, door and window, botanical garden, greenhouse, aquarium, furniture and shower room, etc.
Quality Control:
Conformity to GB/T11944-2002 " the National Standard of Glass"
Product Technical Parameters of ultra-clear glass:
|
Visible |
Visible Light |
Solar Radiant Heat |
U Value |
UV Penet Ration |
||||
Direct Pene |
Reflect |
Absorb |
Total Pene |
W/m2K |
Solar Energy sources Series |
Archite |
|||
3mm |
91.5% |
8% |
91% |
8% |
1% |
91% |
5.8 |
88% |
76% |
3.2mm |
91.5% |
8% |
91% |
8% |
2% |
91% |
5.8 |
88% |
75% |
4mm |
91.4% |
8% |
90% |
8% |
2% |
91% |
5.8 |
87.5% |
73% |
5mm |
91% |
8% |
90% |
8% |
2% |
90% |
5.8 |
87% |
71% |
6mm |
91% |
8% |
89% |
8% |
3% |
90% |
5.7 |
86.5% |
70% |
8mm |
91% |
8% |
88% |
8% |
4% |
89% |
5.7 |
85.4% |
68% |
10mm |
91% |
8% |
88% |
8% |
4% |
89% |
5.6 |
84% |
66% |
12mm |
91% |
8% |
87% |
8% |
5% |
88% |
5.5 |
82.5% |
64% |
15mm |
90% |
8% |
86% |
8% |
6% |
87% |
5.5 |
81% |
61% |
19mm |
90% |
8% |
84% |
8% |
7% |
86% |
5.5 |
78% |
58% |
22mm |
90% |
8% |
82% |
8% |
9% |
85% |
5.5 |
74% |
55% |
Mechanical Parameters of ultra-clear glass:
Elasticity Modulus |
73.1 Gpa |
Rupture Modulus (tensile Strength –ultimate) |
41.4 Mpa |
Knoop hardness |
456kgf/mm² |
Physical Parameters of ultra-clear glass:
Density |
2.5076 g/cm³ |
20~300ºC Linear coefficient of Expansion 20~300ºC |
9.28 x 10-6 /ºC |
Linear Coefficient of Expansion 20~450ºC |
9.75 x 10-6 /ºC |
Transformation Temperature |
556ºC |
Intenerate Temperature or Yield Point |
606ºC |
Softening Point |
710ºC |
Annealing Point |
547ºC |
Strain Point |
513ºC |
Log2 High Temperature Viscosity log2 |
1392ºC |
Log3 High Temperature Viscosity log3 |
1152ºC |
Log4 High Temperature Viscosity log4 |
996ºC |
Liquid Phase Temperature |
1008ºC |
ultra-clear glass